Analisa Kekuatan Tarik dan Bending pada Komposit Widuri-Polyester

Harun Beliu, Yeremias Pell, Jahirwan Jasron

Abstract


The purpose of this study to analyze the tensile strength and flexural strength of widuri fiber reinforced polyester. Treatment with 5% NaOH for 1 hour. Directions random fiber orientation with a fiber size of 1 cm, 3 cm and 5 cm. The test specimen is printed with a printing press method, the fiber volume fraction of 30%, polyester resin binder. The test specimens were performed according to ASTM testing standard ASTM D638 to for tensile and D790 to flexural test. The calculation result obtained an increase in the tensile strength fiber length of 5 cm is 43.0809 MPa. While the value of the highest tensile modulus of elasticity of the fiber length of 3 cm. While testing the flexural obtained the highest bending strength in the fiber length of 3 cm is 62.8874 MPa and flexural strength values were lower in fiber length of 5 cm. While the value of the highest flexural modulus of elasticity of 3.1325 MPa with a fiber length of 5 cm and the lowest fiber length of 3 cm, for the highest value of 6509.916 Nmm flexural moments on the fiber length of 3 cm and the lowest value of flexural moment of the fiber length of 1 cm. From the results of photo fracturing shape tensile test specimens showed that the fiber length of 1 cm, 3 cm, 5 cm is a fault caused by a failure in the weight-bearing matrix. The images form flexural fracture test specimens showed that the fiber length of 5 cm is a fault caused by a failure in the weight-bearing matrix, whereas the fiber length of 1 cm and 3 cm showed the form fracture caused by the failure of fiber in weight-bearing

Keywords


widuri fiber, tensile strength, flexural strength, fiber length

Full Text:

PDF

References


Agil S. Pengaruh Fpraksi Volume Terhadap Sifat Mekanik Komposit Widuri–PolyesterJurusan Teknik Mesin, Fakultas Sains dan Teknik, Universitas Nusa Cendana.

Aji Prasetyaningrum; Nur Rokhati dan Anik Kristi Rahayu.,2009, Optimasi Proses Pembuatan Serat Eceng Gondok Untuk Menghasilkan Komposit Serat Dengan Kualitas Fisik Dan Mekanik Yang Tinggi.

Astika, Lokantar, Karohika., Oktober 2013, Sifat Mekanis Komposit Polyester dengan Penguat Serat Sabut Kelapa. Jurnal Energi dan Manufaktur Vol.6 No.2,: 95-202.

ASTM D790-02, Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and ,Electrical Insulating Materials.

Bakri, Mohammad Iqbal, Mohammad Rifki.,2012 Analisis Variasi Panjang Serat Terhadap Kuat Tarik Dan Lentur Pada Komposit Yang Diperkuat Serat Agave angustifolia Haw, Jurnal Mekanikal, Vol. 3 No. 1: 240-244.

Boimau, Matasina, U.t Jasron., 2014, Pengaruh Perendaman Terhadap Sifat Mekanik Komposit Polyester Berpenguat Serat Buah Lontar.

Bate., 2015, dalam skripsi Pengaruh Panjang Serat dan Fraksi Volume Terhadap Sifat Bending pada Komposit Widuri Polyester

Doni Pa,Yeremias M. Pell, W. Bunganaen., 2014, Pengaruh Perendaman NaoH 5% Terhadap Kekuatan Tarik Serat Widuri. Jurnal Lontar Teknik Mesin Vol. 1 No. 2.

Efri Mahmuda, Shirley Savetlana Dan Sugiyanto., 2013, Pengaruh Panjang Serat Terhadap Kekuatan Tarik Komposit Berpenguat Serat Ijuk Dengan Matrik Epoxy , Jurnal Fema, Volume 1, Nomor 3.

Fahmi, Harry Hermansyah., Oktober 2011, Pengaruh Orientasi Serat Pada Komposit Resin Polyester/ Serat Daun Nenas Terhadap Kekuatan Tarik . Jurnal Teknik Mesin Vol.1, No. 1,: 4652.

Gibson, F Ronald (1994) Principles Of Composite Material Mechanics, McGraw- Hill.

I Putu Lokantara, Ngakan Putu Gede Suardana, I Made Gatot Karohika, Nanda., (2010), Pengaruh Panjang Serat pada Temperatur Uji yang Berbeda Terhadap Kekuatan Tarik Komposit Polyester Serat Tapis Kelapa, Jurnal Ilmiah Teknik Mesin Vol. 4 No.2. (166-172).

M. Budi Nur Rahman, Berli P. Kamiel., 2011, Pengaruh Fraksi Volume Serat terhadap Sifat-sifat Tarik Komposit Diperkuat Unidirectional Serat Tebu dengan Matrik Poliester, Jurnal Ilmiah

Semesta Teknika Vol. 14, No. 2, 133-138.

Nurudin A, Desember 2011, Potensi Pengembangan Komposit Berpenguat Serat Kulit Waru (Hibiscus Tiliaceus) Kontinyu Laminat Sebagai Material Pengganti Fiberglass Pada Pembuatan Lambung Kapal, Info Teknik, Volume 12 No. 2.

Pell, Yeremias, M., 2010, Karakterisasi Perlakuan Permukaan Serat Kulit BatangWiduri (Calotropis gigantea) terhadap Wettability dan Mampu Rekat Serat Tunggal, dan Sifat Mekanik Komposit dengan Matriks Resin Epoksi, Program Studi Teknik Mesin, UGM, Yogyakarta.

Totok Suwanda, Muhammad Budi Nur Rahman, November 2010, Pengaruh Perlakuan Alkali terhadap Kekuatan Ben din g Komposit Berpenguat Serat Rami dengan Matrik Polyester, Jurnal Ilmiah Semesta Teknika Vol. 13, No. 2, 165-170.

Wowa V., 2013, Karakteristik Serat Widuri Akibat Perlakuan NaoH 5% Terhadap Wettability Dan Sifat Mampu Rekat Dengan Resin – Polyester.Jurusan Teknik Mesin, Fakultas Sains dan Teknik, Universitas Nusa Cendana




DOI: http://dx.doi.org/10.0001/ljmtu.v3i2.73

Copyright (c) 2016 LONTAR Jurnal Teknik Mesin Undana (LJTMU )

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.

Diterbitkan oleh Jurusan Teknik Mesin FST Undana; ISSN Cetak: 2356-3222; ISSN Online: 2407-3555; Alamat Redaksi: Jurusan Teknik Mesin; Fakultas Sains dan Teknik; Universitas Nusa Cendana; Jl. Adi Sucipto PO Box 85001, Telp. 0380-881597; Penfui-Kupang NTT.

View My Stats